Super fast-cure series EVA film
Su406&Su806
Product introduction
F?RST? Su406 & Su806 EVA is a super fast-cure type encapsulant product. The lamination time can be decreased to 10min~12min when modules are encapsulated using Su406/Su806 EVA. While the PV module productivity can be greatly increased with Su406 & Su806 EVA, excellent durability, as well as PID and snail trails resistance will be exhibited.
Crosslinking Property
Performance parameter
| Properties | Test Method | Units | Su406 | Su806 | |
| General gram weight | FST Method | g/m2 | 430±20 | 390±20 | |
| Thickness | FST Method | mm | 0.55±0.05 | 0.50±0.05 | |
| Length | FST Method | m/roll | 150 | 150 | |
| Width | FST Method | mm | Customization0/+7 | Customization0/+7 | |
| Density | ASTMD792 | g/cm3 | 0.95-0.96 | 0.95-0.96 | |
| Melting range | FST Method | ℃ | 40-80 | 40-80 | |
| Shrinkage Rate(120℃,3min) | GB/T29848 | MD% | <3.0 | <3.0 | |
| TD% | <1.5 | <1.5 | |||
| UV-Cutoff Wavelength | FST Method | nm | -- | 360 | |
| Transmittance | 1100nm-380nm | GB/T29848 | % | >91 | >91 |
| 380nm-290nm | % | >80 | <30 | ||
| Gel content | GB/T29848 | Gel% | >75 | >75 | |
| Volume Resistivity | GB/T29848 | Ω·cm | >1.0×1015 | >1.0×1015 | |
| Strength of Peeling from Glass | GB/T29848 | N/cm | >60 | >60 | |
| Strength of Peeling from TPT | GB/T29848 | N/cm | >40 | >40 | |